スーパー二相ステンレス鋼316よりもはるかに高い強度と耐食性を提供します。したがって、答えは「はい」です。スーパーデュプレックスは316よりも優れています。316.
'Duplex' stainless steels are a family of stainless steels that contain a mixed microstructure of austenite and ferrite phases. They offer a combination of good corrosion resistance and high strength, making them suitable for a wide range of applications. Super duplex stainless steels have a higher content of alloying elements, such as chromium, nickel, and molybdenum, compared to duplex stainless steels. They are based upon 25% chromium content. As such, super duplex stainless steels have up to four times the tensile strength of 316 stainless steel, and considerably better corrosion resistance. An alloys resistance to pitting corrosion can be usefully summarised by the PREN value, which is the 'Pitting Resistance Equivalent number'. The PREN for super duplex stainless steels is >40 で、PREN は 25 件中 316 件でした。
しかし、スーパー二相ステンレス鋼は316よりも非常に魅力的な利点があるにもかかわらず、いくつかの制限があります。スーパー二相ステンレス鋼は-50度C以下で衝撃靭性が大幅に低下しますが、316では衝撃靭性は極低温までほぼ維持されます。スーパー二相ステンレス鋼は250度C以下の長期動作温度に制限されていますが、316は870度Cまで使用できます（低炭素鋼であれば）。316Lまたは、粒界腐食を避けるためにチタン安定化 316Ti バリアントを使用します。
スーパー二相ステンレス鋼は、強度がはるかに高いため、機械加工が困難であることは確かです。溶接が難しいと思われていますが、適切な設備と手順を使用すれば簡単に加工できます。